Udimet L605 Sheet, Udimet L605 Sheet Importers, Udimet L605 Sheet Suppliers, Udimet L605 Sheet Exporter, Udimet L605 Sheet Stockists.
Udimet L605 Sheet in India, Udimet L605 Sheet Importers in India, Udimet L605 Sheet Suppliers in India, Udimet L605 Sheet Exporter in India, Udimet L605 Sheet Stockists in India.
Udimet L605 Sheet in Mumbai, Udimet L605 Sheet Importers in Mumbai, Udimet L605 Sheet Suppliers in Mumbai, Udimet L605 Sheet Exporters in Mumbai, Udimet L605 Sheet Stockists in Mumbai.
HY L-605 is useful in gas turbine applications such as rings,blades and combustion chamber parts (sheet fabrications) and can also can be used in industrial furnace applications such as muffles or liners in high temperature kilns
HY L605 is a solid solution strengthened cobalt-chromium-tungstennickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°C). The alloy also offers good resistance to sulfidation and resistance to wear and galling.
| Chemical Composition Limits | ||||||||||
| Weight% | C | P | Si | Ni | W | Mn | S | Cr | Co | Fe |
| Alloy L-605 | 0.05 - 0.15 | 0.040 max | 0.40 max | 9.0 - 11.0 | 14.0 - 16.0 | 1.0 - 2.0 | 0.030 max | 19.0 - 21.0 | Bal | 3.0 max |
Typical Mechanical Properties
| Material | Temperature °F | Yield Strength 0.2% | Tensile Strength | Elongation (%) | Hardness HB |
| Extruded Bar Alloy 25 / L-605 |
RT | 310 Mpa 45 KSI |
862 Mpa 125 KSI |
30 | 277 max |
| Material Sheet |
Thickness (inches) | Yield Strength 0.2% KSI |
Tensile Strength KSI min |
Elongation (%) | Hardness HRC |
| Alloy 25 / L-605 Solution Treated (AMS 5537) |
0.005-0.020 | 55-80 | 130 | 30 | - |
| Alloy 25 / L-605 Solution Treated (AMS 5537) |
0.020-0.032 | 55-80 | 130 | 35 | - |
| Alloy 25 / L-605 Solution Treated (AMS 5537) |
0.032-0.043 | 55-80 | 130 | 40 | - |
| Alloy 25 / L-605 Solution Treated (AMS 5537) |
0.043-0225 | 55-80 | 130 | 45 | - |